The effects of oxidizers on the diameters of the carbon naotubes grown by chemical vapor deposition method

No Thumbnail Available

Date

2012

Journal Title

Journal ISSN

Volume Title

Publisher

Izmir Institute of Technology

Open Access Color

Green Open Access

Yes

OpenAIRE Downloads

OpenAIRE Views

Publicly Funded

No

Research Projects

Organizational Units

Journal Issue

Events

Abstract

This thesis was focused on growing high quality and small-diameter carbon (C) nanotube (NT) on Fe/Al2O3/SiO2/Si thin film catalyst by ethylene decomposition thermal chemical vapor deposition (CVD) method in the presence of a weak oxidizer (CO2). Moreover, the importance and functional properties of the oxidizer in pretreatment and CNT growth were determined. At first, it was worked in different growth conditions to examine the effects of CO2 in CNT growth. The main parameters were pretreatment time, CO2 gas flow rates during pretreatment and growth, growth temperature. Pretreatment and growth times were kept at 15 min. each and CO2 introduced 5 and 10 min. during pretreatment stage prior to the CNT growth with the flow rates 8:2, 10:2, 10:8 and 10:10 sccm, respectively. Additionally, three different growth temperatures; 750 oC, 760 oC and 770 oC were studied. Secondly, pretreatment time was kept at 15 min. The effects of CO2, which was sent in the system at 8:2, 10:2, 10:8 and 10:10 sccm ratios, on density and height of the catalyst particles were investigated. At last, all catalyst particles and CNTs obtained from the experiments were analyzed by several characterization techniques such as AFM, EDX, SEM, STEM and Raman Spectroscopy, respectively. The optimal values of amount and introduction time of CO2, the ratio of CO2 in growth to that in pretreatment were identified. Moreover, the relation between currently obtained catalyst particles and previously being grown CNTs on them were determined. It was observed that using the appropriate amount of CO2 in pretreatment and growth process positively affected the catalyst sizes and CNT diameter distributions.

Description

Thesis (Master)--Izmir Institute of Technology, Physics, Izmir, 2012
Includes bibliographical references (leaves: 98-105)
Text in English; Abstract: Turkish and English
xv, 105 leaves

Keywords

Fizik ve Fizik Mühendisliği, Physics and Physics Engineering

Turkish CoHE Thesis Center URL

Fields of Science

Citation

WoS Q

Scopus Q

Source

Volume

Issue

Start Page

End Page

Collections