Çakicioğlu Özkan, Seher FehimeÇiçek, Ahmet Uğur2023-11-132023-11-132014http://standard-demo.gcris.com/handle/123456789/5055Thesis (Master)--Izmir Institute of Technology, Chemical Engineering, Izmir, 2014Full text release delayed at author's request until 2018.01.19Includes bibliographical references (leaves: 69-76)Text in English; Abstract: Turkish and Englishxii, 76 leavesIn this study, synthesis of Copper based metal organic framework (CuTPA) was achieved. Terephthalic acids were used as an organic linkers supplied from PETKİM A.Ş. Synthesis procedure was carried out in three steps; crystallization, purification and activation with different parameters. Crystallization time and temperature, purification method and solvent type , thermal activation rate are studied. MOFs were characterized by using SEM (Scanning Electron Microscopy), Fourier Transformer Infrared (FTIR), Thermal Gravimetric Analyzer (TGA), X-ray Diffractometer (XRD), and Volumetric Adsorption Instrument (ASAP 2010). The CuTPA with the highest specific surface area (SLang=776 m2/g) was synthesized after purification with methanol by soxhlet method in a schott bottle for 24 hours at crystallization temperature of 110 oC. Copper based MOF synthesized (SLang=776 m2/g) and Commercial NaX zeolite (SLang= 1359 m2/g) were packed in the column. Dynamic adsorption behavior of adsorbents was also studied; breakthrough of CO2/H2 and gases from the packed bed were carried out under total molar flow rate of 10, 20, and 30 mL/min gas mixture at 1, 5, and, 10 bars. It was conclude that the adsorption data results obtained from our system is reliable. As a result of breakthrough experiment both adsorbents (CuTPA and 13X zeolite) did not adsorbed H2. The break points are increased with increasing pressure and decreasing total flow rate. The amount to be adsorbed by the adsorbent in the column is increased indicating that the adsorption mechanism, controlling mechanism is changed with decreasing total flow rate.eninfo:eu-repo/semantics/openAccessMetal organic frameworkCopper terephthalateGas separationHydrogenMaster Thesis